| Lines 1-4 were replaced by lines 1-7 |
| - ||Name||Description ||T-range||sample\\space\\diameter||Thread on stick |
| - |[FS]|small furnace |350...700 K |50|M6 female |
| - |[FT]|tantalum furnace|375...1400 K|50|M6 female |
| - |[FI]|ILL-type furnace|500...1800 K|40|M8 male |
| + ||Name||Description ||T-range||sample\\space\\diameter||max.\\sample\\diameter||Thread on stick| sample length |
| + |[FS]|small furnace |350...700 K |25*| |M6 female| <70 |
| + |[FT]|tantalum furnace|375...1400 K|50|45|M6 female| |
| + |[FI]|ILL-type furnace\\__temporary out of service__|500...1800 K|40|35|M8 male| |
| + |[FFTF]|fast ramping thin film furnace|300...900 K| 10|10|clamped|thinfilm substrate |
| + (*) 50 mm without radiation screen. However, in this mode very large temperature |
| + gradients are expected. |
| Removed line 10 |
| - |
| Line 13 was replaced by line 15 |
| - samples, please check the phase diagrams of possible allows |
| + samples, please check the phase diagrams of possible alloys |
| At line 21 added 7 lines. |
| + * __never use Cadmium or Indium in a furnace__, even not at relatively 'low' temperatures |
| + |
| + The pictures below shows what might happen, if these rules are not |
| + obeyed. |
| + |
| + [FurnaceList/moltenSample.jpg] |
| + \\Picture 1: Reaction of the sample with the container. |
| Lines 23-24 were replaced by lines 32-36 |
| - The picture below shows what might happen, if these rules are not |
| - obeyed. [FurnaceList/moltenSample.jpg] |
| + [FurnaceList/ftCd1.jpg] |
| + [FurnaceList/ftCd2.jpg] |
| + [FurnaceList/ftCd3.jpg] |
| + [FurnaceList/ftCd4.jpg] |
| + \\Picture 2,3,4,5: Molten and condensed Cadmium. |
LIN